@ -515,3 +515,119 @@ This is value is known as the fracture toughness, $K_c$.
|
|||||||
|
|
||||||
At low thicknesses fracture toughness depends on thickness but as thickness increases, $K_c$
|
At low thicknesses fracture toughness depends on thickness but as thickness increases, $K_c$
|
||||||
decreases to the constant value, the plane strain fracture toughness, $K_{1c}$.
|
decreases to the constant value, the plane strain fracture toughness, $K_{1c}$.
|
||||||
|
|
||||||
|
# Composites
|
||||||
|
|
||||||
|
Composites are made of two or more materials, which when combined together, at up to a milimetre
|
||||||
|
scale, have superior properties to their parent materials.
|
||||||
|
|
||||||
|
Composites tend to be 2-phase: a dispersed phase in a matrix.
|
||||||
|
The disepersed phase tends to be fibres (large aspect ratio) or particles (low aspect ratio) which
|
||||||
|
are embedded in a matrix, which are often resins.
|
||||||
|
|
||||||
|
Composite properites are affected by the dispersed phase geometry:
|
||||||
|
|
||||||
|
- Shape
|
||||||
|
- Size
|
||||||
|
- Distribution
|
||||||
|
- Relative orientation (for fibres)
|
||||||
|
|
||||||
|
## Rule of Mixtures
|
||||||
|
|
||||||
|
$E_c$ lies between the arithmetic mean (upper limit):
|
||||||
|
|
||||||
|
$$V_mE_m + E_pV_p$$
|
||||||
|
|
||||||
|
and the geometric mean (lower limit):
|
||||||
|
|
||||||
|
$$\frac{V_mE_mE_pV_p}{V_mE_m + E_pV_p}$$
|
||||||
|
|
||||||
|
Where $E_c$, $E_m$, $E_p$ are the Young's moduluses of the composite, matrix, and particles,
|
||||||
|
respectively, and $V_m$ and $V_p$ are the volume of the matrix and particles, respectively.
|
||||||
|
|
||||||
|
## Particle Reinforced Composites
|
||||||
|
|
||||||
|
### Applications of Composites
|
||||||
|
|
||||||
|
<details>
|
||||||
|
<summary>
|
||||||
|
|
||||||
|
#### Tungsten Carbide Cobalt for Cutting Tools
|
||||||
|
|
||||||
|
</summary>
|
||||||
|
|
||||||
|
The Tungest Carbide (WC) particle are a truly brittle ceramic.
|
||||||
|
They are very hard but the brittleness means they are easy to break.
|
||||||
|
|
||||||
|
The solution is to hold small WC particles in a ducitle metal matrix.
|
||||||
|
In this case it is Cobalt (Co).
|
||||||
|
|
||||||
|
This way, crack in one WC particle does not necessarily mean other particles are broken,
|
||||||
|
meaning the cutting tool overall still works.
|
||||||
|
|
||||||
|
Another advantage of this composite is that WC is not very thermally conductive and has a high
|
||||||
|
melting point, which allows it to work well the environment it's in.
|
||||||
|
|
||||||
|
</details>
|
||||||
|
|
||||||
|
<details>
|
||||||
|
<summary>
|
||||||
|
|
||||||
|
#### Resin Bonded Alumina for Sanding Disks
|
||||||
|
|
||||||
|
</summary>
|
||||||
|
|
||||||
|
This is another example of brittle but hard ceramics being put in a ductile matrix.
|
||||||
|
In this case it's a resin.
|
||||||
|
|
||||||
|
It follows the same idea---separating the ceramics into small particles means the particles can
|
||||||
|
break and the product still works overall, as there are thousands of particles which are not broken.
|
||||||
|
</details>
|
||||||
|
|
||||||
|
## Fibre Reinforced Composites
|
||||||
|
|
||||||
|
### Specific Property
|
||||||
|
|
||||||
|
Specific Property of a composite is a property divided by density of composite.
|
||||||
|
Here are some examples of specific properties:
|
||||||
|
|
||||||
|
- Specific ultimate tensile stress $= \frac{\sigma_{UTS}}{\rho_c}$
|
||||||
|
- Specific Young's modulus/stiffness $= \frac{E_c}{\rho_c}$
|
||||||
|
|
||||||
|
### Influence of the Fibres
|
||||||
|
|
||||||
|
Depends on:
|
||||||
|
|
||||||
|
- Fibre type
|
||||||
|
- Fibre length and diameter
|
||||||
|
- Fibre orientation
|
||||||
|
- Strength of bond between fibre and matrix
|
||||||
|
|
||||||
|
### Stress Strain Graph of a Fibre Reinforced Composite
|
||||||
|
|
||||||
|

|
||||||
|
|
||||||
|
Note that the composite fails at the same strain as the fibres but yields at the same strain as
|
||||||
|
the polymer matrix.
|
||||||
|
|
||||||
|
The elastic behaviour of the composite before yielding is dependent on the strength of the chemical
|
||||||
|
bonds between the surface of the fibre and matrix.
|
||||||
|
|
||||||
|
### Mechanical Performance of a Fibre Reinforced Composite
|
||||||
|
|
||||||
|
- Stress/strain behaviour of fibre
|
||||||
|
- Stress/strain behaviour of matrix
|
||||||
|
- Fibre volume fraction
|
||||||
|
- Applied stress direction
|
||||||
|
|
||||||
|
Longitudinal is along direction of fibres, transverse is 90\textdegree to direction.
|
||||||
|
|
||||||
|
Fibre composites tend to be much much weaker in transverse direction:
|
||||||
|
|
||||||
|
Composite | Longitudinal UTS | Transverse UTS
|
||||||
|
------------ | ---------------- | --------------
|
||||||
|
GF/PET | 700 | 20
|
||||||
|
CF/Epoxy | 1000 | 35
|
||||||
|
Kevlar/Epoxy | 1200 | 20
|
||||||
|
|
||||||
|
(All units in MPa)
|
||||||
|