Lecture 1 (2021-10-04)

1A Reading Notes

Classification of Energy-Related Materials

• Passive materials---do not take part in energy conversion e.g. structures in pipelines, turbine blades, oil drills

• Active materials---directly take part in energy conversion e.g. solar cells, batteries, catalysts, superconducting magnests

• The material and chemical problems for conventional energy systems are mostly well understood and usually associated wit structural and mechanical properties or long standing chemical effects like corrosion:

  • fossil fuels
  • hydroelectric
  • oil from shale and tar
  • sands
  • coal gasification
  • liquefaction
  • geothermal energy
  • wind power
  • bomass conversion
  • solar cells
  • nuclear reactors

Applications of Energy-Related Materials

High Temperature Materials (and Theoretical Thermodynamic Efficiency)

• Thermodynamics indicated that the higher the temperature, the greater the efficiency of heat to work:

   \frac{ T_{high} - T_{low} }{ T_{high} } 

• The first steam engines were only 1% efficient, while modern steam engines are 35% efficient primarily due to improved high-temperature materials.

• Early engines made from cast iron while modern engines made from alloys containing nickel, molybdenum, chromium, and silicon, which don't fail at temperature above 540 \textdegree{}C

• Modern combustion engines are nearing the limits of metals so new materials that can function at even higher temperatures must be found--- particularly intermetallic compounds and ceramics are being developed

Types of Stainless Steel

• Type 304---common; iron, carbon, nickel, and chromium
• Type 316---expensive; iron, carbon, chromium, nickel, molybdenum

Self Quiz 1

1. What is made of billion year old carbon + water + sprinkling of stardust?

   Me

2. What are the main classifications of materials?

   Metals, glass and ceramics, plastics, elastomers, polymers, composites, and semiconductors

3. [There are] Few Iron Age artefacts left. Why?

   They rusted away

4. What is maens by 'the micro-structure of a material'?

   The very small scale structure of a material which can have strong influence on its physical properties like toughness and ductility and corrosion resistance

5. What is a 'micrograph' of a material?

   A picture taken through a microscope

6. What microscope is used to investage the microstructure of a material down to a 1 micron scale resolution?

   Optical Microscope

7. What microscope is used [to investigate] the microstructure of a material down to a 100 nm scale resolution?

   Scanning Electron Microscope

8. What length scales did you see in the first slide set?

   1 mm, 0.5 mm, 1.5 \textmu{}m

9. What material properties were mentioned in the first slide set?

   Hardness, brittleness, melting point, corrosion, density, thermal insulation

Self Quiz 2

1. What is the effect of lowering the temperature of rubber?

   Makes it more brittle, much less elastic and flexible

2. What material properties were mentioned in the second slide set?

   Young's modulus, specific heat, coefficient of thermal expansion

Lecture 2

Properties of the Classes

Metals

• Ductile (yields before fracture)
• High UFS (Ultimate Fracture Stress) in tension and compression
• Hard
• Tough
• High melting point
• High electric and thermal conductivity

Ceramics and Glasses

• Brittle --- elastic to failure, no yield
• Hard (harder than metals)
• Low UFS under tension
• High UFS under compression
• Not tough
• High melting points
• Do not burn as oxide ceramics are already oxides
• Chemically resistant
• Poor thermal and electric conductivity
• Wide range of magnetic and dielectric behaviours

Polymers

• Organic---as in organic chemistry (i.e. carbon based)

• Ductile

• Low UFS in tension and compression

• Not hard

• Reasonably tough

• Low threshold temperature to charring and combustion in air or pure oxygen

• Low electrical and thermal conductivity

  • There are some electrically conductive polymers

Composites

• Composed of 2 or more materials on any scale from atomic to mm scale to produce properties that cannot be obtained in a single material

  • Larger scale mixes of materials may be called 'multimaterial'

• Material propertes depends on what its made of

Terms

Organic vs Inorganic Materials

• Organic materials are carbon based
• From chemistry, organic compounds are ones with a C-H bond
• Inorganic compounds do not contain the C-H bond

Crystalline vs Non-Crystalline Materials

• Most things are crystalline

  • Ice
  • Sugar
  • Salt
  • Metals
  • Ceramics

• Glasses are non-crystalline

Material Properties

Density

\rho = \frac m v

• Density if quoted at STP (standard temperature and pressure---298 K and 1.013\times 10^5 Pa)

• Metals, ceramics, and glasses are high density materials

• Polymers are low density

• Composites span a wide range of density as it depends on the materials it is composed of

  e.g. composites with a metal matrix will have a much higher density than those with a polymer matrix

Melting Points

• Measured at standard pressure and in an intert atmosphere (e.g. with Nitrogen, Argon, etc)

  • Diamond and graphite will survive up to 4000 \textdegree{}C in an inert atmosphere but would burn at around 1000 \textdegree{}C in oxygen

• High melting points -> high chemical bond strength

Corrosion

• It's not just metals that corrode

• Polymers

  • UV degradation
  • Water absorption can occur in degraded polymers

• Glass

  • Leaching
  • Sodium ions can leave the glass when covered in water. If the water stays, the high pH water can damage the class

Self Quiz

Consolidation Questions 1

i. Metal ii. Titanium

2. i. Polymer ii. Polyester

i. Ceramic ii. Alumino-silicate

i. Composite ii. GFRP or CFRP

i. Metal ii. Aluiminium alloy

i. Metal ii. Aluiminium alloy

i. Polymer ii. Acrylic

i. Ceramimc ii. Glass

i. Composite ii. Concrete

Consolidation Questions 2

C B

Polymers

Introduction to Polymers

There are 3 types of polymers:

• thermoplastics

  

  No cross links between chains. The lack of cross links allows recycling of polymers by heating it above the glass transition material, T_g, lowering the viscosity.

  An example of thermoplastics is PET, used in water bottles

• thermosets

  

  has lots of cross-links between chains, making it more rigid. Heating does not lower its viscosity making them much harder/impossible to recycle.

  and example of thermosets is melamine formaldehyde, used on kitchen tabletops

• elastomers

  

  has some cross links and a lot of folding of chains

  Latex is an example of an elastomer

Polymers are relatively new materials, lightweight, durable, flammable, and degraded by UV light. They are made of long carbon-carbon chains.

Stress-Strain Curve of Polymers

Industrially Important Polymers

The worldwide production of polymers in 2019 was 368\times10^6 tonnes and the majority is from just 5 polymers:

• Polyethylene (PE) --- wire insulation, flexible tubing, squeezy bottles
• Polypropyene (PP) --- carpet fibres, ropes, liquid containers, pipes, chairs in Shoreham Academy
• Polyvinyl chloride (PVC) --- bottles, hoses, pipes, valves, wire insulation, toys
• Polystyrene (PS) --- packaging foam, egg cartons, lighting panels
• Polyethylene terephthalate (PET) --- carbonated drinks bottles

All of these materials are low cost.

Thermoplastics

The simplest polymer is poly(ethene):

When 2 polymer chains get close together, Van der Waals (vdw) forces keep them together. vdw forces are very weak, much weaker than the covalent bonds inside the polymer.

Stress Strain Curve

• During linear deformation, the carbon chains are strethed.
• At yield stress, the carbon chains get untangled and slide past eache other.
• Necking initially allows the chains to slide at lower stress.
• As the chains pull, align, and get closer, the vdw forces get stronger and more stress is required to fracture.

Crystalline and Amorphous/Glassy Solids (Heating and Cooling)

Amorphous Thermoplastics

• As you heat above T_g, the chains get easier to move past each other.
• It is known as an amorphous supercooled liquid.
• There is not really a melting point are there are no crystals, but T_m is the point where the chains are easy to move

Crystalline Polymers

• The glass transition point does not exist for crystalline polymers
• The solid is difficult to deform below T_m and is not ductile
• Above T_m the chains are very easy to move past each other

Semi-Crystalline

• Below T_g, only local movements in chains are possible, so the material is less ductile. The solid crystalline regions makes it difficult to move the chains.
• Between T_g and T_m, the glassy chains are easier to move but the crystalline regions remain difficult
• Above T_m the chains easily move past each other

Specific Volume vs Temperature

Path ABCD

• a-b --- Start cooling the true liquid
• b-c --- At the freezing point, T_m, the true liquid freezes diretly to a crystalline solid
• c-d --- The crystalline solid cools t room temperature as the temperature is lowered

Path ABEF

• a-b --- start cooling the true liquid

• b --- at the freezing point nothing freezes

• b-e --- the liquid becomes supercooled and contracts and becomes more viscous as the temperature decreases.

  The supercooled liquid region is between T_g and T_m

  Supercooling requires you to cool the sample quicker than you would for path ABCD

• e --- T_g is reached and the supercooled liquid sets to a amorphous solid

• e-f --- the amorphous solid cools from room temperature and contract as the temperature is lowered

Relative Molar Mass and Degree of Polymerisation

• Number Average RMM --- \bar M_n = \sum x_iM_i
• Weight Average RMM --- \bar M_w = \sum w_iM_i
• Degree of polymerisation --- n_n = \frac {\bar M_n} m and n_w = \frac {\bar M_w} m

where

• M_i is the RMM of the chain
• x_i is the fraction of the polymer that is composed of that chain by number/quantity
• w_i is the fraction of the polymer that is composed of that chain by mass/weight
• m is the RMM of the monomer from which the polymer was made

Making Polymers

There are two ways to make polymers:

• Addition Poymerisation
• Condensation Polymerisation

Elastic Deformaion

Elastic deformation is deformation where the material will return to original shape after the applied stresses are removed.

Elastic deformation is the first type of deformation that happens when stresses are applied to a material and is represented by the straight line at the beginning of a stress-strain curve.

Modulus of Resillience (E_r)

This is the area under the elastic portion of a stress-strain graph of a material.

Plastic Deformation

Toughness (Absorbing Energy Through Plastic Deformation)

• The toughness of a material is its ability to absorb energy through plastic deformation without fracturing
• The material toughness of a ductile material can be determined by finding the area under its stress-strain curve (e.g. by integrating the graph)
• Brittle materials like ceramics and glasses exhibit no material toughness
• Ductile materials have a possibility of achieving large material toughness

Ductility measures how much something deforms plastically before fracture, but just because a material is ductile does not make it tough.

The key to high material toughness is a good combination of large ultimate fracture stress and large ductility.

• The unit of toughness is energy per unit volume as toughness can be mathematically expressed as:

  toughness = \int^{\varepsilon_f}_0\! \sigma \,\mathrm{d}\varepsilon 
    = \frac{\text{Energy}}{\text{Volume}} $$
  
  

• A metal may have satisfactory toughness under static loads but fail under dynamic loads or impact

  This may be caused by the fact that ductility and toughness usually decrease as rate of loading increases.

• Ductility and toughness decreasee with temperature

• Notches in the material affect the distribution of stress in the material, potentially changing it from a uniaxial stress to multiaxial stress

Charpy Impact Test

Measures material toughness by determining the amount of energy absorbed during fracture.

It works by essentially dropping a hammer into a sample whose dimensions are standardized (usually either by BSI or ISO) and measuring how high the hammer goes up on the other side, after it breaks the material

The height of the hammer after impact will tell you how much enery is left in it, and therefore how much has been aborbed by the now broken sample.

Under a microscope, more ductile fractures appear fibrous or dull, whereas less ductile surfaces have granular or shiny surface texture.A

The charpy test has a couple issues:

• Results are prone to scatter as it is difficult to achieve a perfectly shaped notch
• Temperature has to be strictly controlled since it affects a material's ductility

The setup of a charpy impact test

1. Sample is made to standardized dimensions, with a notch
2. Sample is placed on support
3. A very heavy hammer pendulum of mass m is dropped from rest at h_0 to swing about a pivot, reaching E_{kmax} vertically below the pivot.

a. If no sample is in place then the hammer will swing back up on the other side to a height of h_h where theoretically $h_h = h_0$ b. With a sample placed vertically below, some of the E_k is transferred to the sample to bend and (usually) break the sample.

  If breaks the sample, it will swing up to the other side, where its max height, $h_f$ can be
  used to calculate how much energy was used to break the sample:

  $$E = mg(h_h-h_f)$$

  Where $g$ is acceleration due to gravity.

Ductility

Ductility is the plastic deformation a material withstands before fracture.

Griffith Surface Flaws

These flaws vary in size and shape. They limit the ability of any material, brittle or ductile, to withstand tensile stresses as they concentrate the tensile forces applied to a smaller area.

The stress at the tip of the flaw:

\sigma_{actual} = 2\sigma\sqrt{\frac a r}

For deep (a is large) or thin (r is small) the stress is magnified and, if it exceeds the UFS in a brittle material, the flaw will grow into a crack, resulting in the brittle material fracturing.

However in a ductile material, the tip of the flaw can heal, reducing a and increasing r. This is due to the chemical structure of ductile materials like metals.

Stress Intensity Factor

Stress Intesity Factor, K:

K = f\sigma\sqrt{\pi a}

where:

• f is the geometry factor (1 would represent an infinite width sample, and 0 a 0 width sample)
• \sigma is applied tensile strength
• a is flaw depth

Fracture Toughness

The value of K that causes the notch to grow and cause fractures. This is value is known as the fracture toughness, K_c.

At low thicknesses fracture toughness depends on thickness but as thickness increases, $K_c$ decreases to the constant value, the plane strain fracture toughness, K_{1c}.

Composites

Composites are made of two or more materials, which when combined together, at up to a milimetre scale, have superior properties to their parent materials.

Composites tend to be 2-phase: a dispersed phase in a matrix. The disepersed phase tends to be fibres (large aspect ratio) or particles (low aspect ratio) which are embedded in a matrix, which are often resins.

Composite properites are affected by the dispersed phase geometry:

• Shape
• Size
• Distribution
• Relative orientation (for fibres)

Rule of Mixtures

E_c lies between the arithmetic mean (upper limit):

V_mE_m + E_pV_p

and the geometric mean (lower limit):

\frac{V_mE_mE_pV_p}{V_mE_m + E_pV_p}

Where E_c, E_m, E_p are the Young's moduluses of the composite, matrix, and particles, respectively, and V_m and V_p are the volume of the matrix and particles, respectively.

Particle Reinforced Composites

Applications of Composites

Tungsten Carbide Cobalt for Cutting Tools

The Tungest Carbide (WC) particle are a truly brittle ceramic. They are very hard but the brittleness means they are easy to break.

The solution is to hold small WC particles in a ducitle metal matrix. In this case it is Cobalt (Co).

This way, crack in one WC particle does not necessarily mean other particles are broken, meaning the cutting tool overall still works.

Another advantage of this composite is that WC is not very thermally conductive and has a high melting point, which allows it to work well the environment it's in.

Resin Bonded Alumina for Sanding Disks

This is another example of brittle but hard ceramics being put in a ductile matrix. In this case it's a resin.

It follows the same idea---separating the ceramics into small particles means the particles can break and the product still works overall, as there are thousands of particles which are not broken.

Fibre Reinforced Composites

Specific Property

Specific Property of a composite is a property divided by density of composite. Here are some examples of specific properties:

• Specific ultimate tensile stress = \frac{\sigma_{UTS}}{\rho_c}
• Specific Young's modulus/stiffness = \frac{E_c}{\rho_c}

Influence of the Fibres

Depends on:

• Fibre type
• Fibre length and diameter
• Fibre orientation
• Strength of bond between fibre and matrix

Stress Strain Graph of a Fibre Reinforced Composite

Note that the composite fails at the same strain as the fibres but yields at the same strain as the polymer matrix.

The elastic behaviour of the composite before yielding is dependent on the strength of the chemical bonds between the surface of the fibre and matrix.

Mechanical Performance of a Fibre Reinforced Composite

• Stress/strain behaviour of fibre

• Stress/strain behaviour of matrix

• Fibre volume fraction

• Applied stress direction

  Longitudinal is along direction of fibres, transverse is 90\textdegree to direction.

  Fibre composites tend to be much much weaker in transverse direction:

  Composite	Longitudinal UTS	Transverse UTS
  GF/PET	700	20
  CF/Epoxy	1000	35
  Kevlar/Epoxy	1200	20

  (All units in MPa)

Thermal Properties of Materials

Specific Heat Capacity

How much heat energy is required to raise the temperature of a body by one unit:

 C_p = \frac{\Delta E}{m\Delta T} 

where c is specific heat capacity.

It is measured at a constant pressure, usually 1.013\times 10^5 Pa.

Molar Heat Capacity

C_pm = \frac{\Delta E}{n\Delta T}

What is a mole?

The mole (symbol: mol) is the base unit of amount of substance in the International System of Units (SI). It is defined as exactly 6.02214076\times 10^{23} elementary entities ("particles")

~ Wikipedia: Mole (unit)

How Much Does a mol of Something weigh?

A mol of an element weighs its relative atomic mass (A_r) but in grams. For example, Carbon-12 has an A_r of 12 (as it's made of 6 neutrons, 6 protons, and 6 electrons which have negligible mass) so a mol of Carbon-12 has a mass of 12 g.

Thermal Expansion

Origin of Thermal Expansion

All atomic bonds vibrate, on the magnitude of gigahertz. The bonds vibrate about a mean positoin and the vibration is a simple harmonic motion.

From the graph below you can see that as energy (in the form of heat) is supplied to the bonds, the amplitude of the vibrations get larger and larger. You can also see the mean position of the bond gets further and further away, meaning the volume of the material also is increasing. The mean position of the bond is what dictates the volume, as this means the inter-atomic separation increases.

Morse potential is the energy well between 2 bonded atoms. The graph is asymmetric due to the repulsion experienced by atoms as they apporach.

Linear Coefficient of Thermal Expansion

\alpha_L = \frac{\Delta L}{L_0 \Delta T}

where L is the sample length.

Example 1

A 1 m long bar of aluminium metal cools in the solid state from 660 \textdegree{}C to 25 \textdegree{}C.
Calculate the length of the bar after it cools down, given \alpha_L = 25\times10^{-6} K$^{-1}$.

\begin{align*} l_0 &= 1 \ \Delta T &= T_f - T_0 = 25 - 660 = -635 \ \ \alpha_L &= \frac{l_f - l_0}{l_0 \Delta T} \ \alpha_L l_0 \Delta T &= l_f - l_0 \ l_f &= \alpha_L l_0 \Delta T + l_0 = 0.984 \end{align*}

Linear Thermal Expansion and Isotropism

Since isotropic solids have the same properties in all directions, you can say that for an isotropic solid:

\alpha_V = 3\alpha_L = \frac{\Delta V}{V_0 \Delta T}

Reasons to Care About Thermal Expansion

• A coating on a material may fail if the thermal expansion coefficients do not match
• A brittle material may thermally shock and fracture due to thermal expansion mismatch between the ouside and inside, especially if the material is not very thermally conductive

Thermal Conductivity

Thermal conductivity is the rate at which heat power is transferred through a material.

\frac{Q}{A}  = k \frac{\Delta T}{\Delta x}

where Q is heat power, A is area of the surface, \frac{\Delta T}{\Delta x} is the temperature gradient, and k is the thermal conductivity constant.

Origin of Thermal Conductivity

Heat is transferred through materials by electrons (and partially by atomic vibrations)

Metals have high thermal conductivity as their delocalised 'sea' electrons are about to move about easily. This makes them excellent conductors of heat and electricity.

Ceramics, glasses, and polymers do not have delocalised electrons and are therefore poor conductors of heat and electricity (they are insulators).

Polymer foams are even better insulators because they have holes which lowers their density.

Chemical Bonding of Materials

Chemical bonds are what holds a material together in solid state. There are 5 main types of bonds:

Type	Dissociation energy
Ionic	600 to 1500
Covalent	300 to 1200
Metallic	100 to 800
Hydrogen	4 to 23
vdw	0.4 to 4

The dissociation energy is the energy required to break the bond, or the strength of the bond.

Materials and their Properties and Bonding

Ceramics and Glasses

Ceramics and glasses are composed of mixed ionic and covalent bonding. Their strong and rigid bonds have no ability to slide past each other. This makes the materials brittle.

Metals

Metals are based on metallic bonding (woah). This type of bonding does allow for ions to slide past each other, making metals ductile.

Polymers

Polymer chains made of C-C covalent bonds are strong, like those found in ceramics.

However, in thermoplastics polymers, the materials can yield by having the chains untangle and then align, as the chains slide past each other. This means that stronger bonds between polymer chains means a higher yield stress in thermoplastic polymers.

Crystallisation of Materials

Atomic Arrangement

• No order

• Short range order

  Silica glasses have short range order on the atomic scale. They are composed of regular SiO$_4$ units which all have the same bond length and bond angles.

  However, these units bond together irregularly, which results in different length chemical bonds and angles between the units, meaning they do not have any long range order.

• Long range order

Cubic Unit Cells

• Lattice Parameter --- One side of a unit cell

  The lattice parameter can be different for each side of a cell.

• Simple cubic unit (SC):

  

  Lattice Parameter = 2r

• Face centred cubic (FCC)

  

• Body centred cubic (BCC)

  

Packing Factor

\text{packing factor} = \frac{\text{ions per unit cell} \times V_{ion}}{V_{cell}}

Theoretical Density

\text{theoretical density} = \frac{\text{ions per unit cell} \times m_{ion}}{V_{cell}}

Polymorphism

Example of a polymorphic solid-state phase transfomration of iron at 1185 K and 1 atm:

\text{Fe}_{\text{BCC}} \longleftrightarrow \text{Fe}_{\text{FCC}}

Below 1185 K and at 1 atm, only BCC exists. Above 1185 K and at 1 atm, only FCC exists.

Points, Directions, Planes in a Cubic Unit Cell

Slip Systems in Metals

Metal ions lying in close-packed planes and directions move more easily, increasing ductility. The combination of a close packed plane and direction is called a slip system.

A close packed direction is where ions touch all the way along the direction.

A close packed plane is where ions touch all the way on a plane.

FCC metal ductility is mainly controlled by the (111) slip plane

X-Ray Diffraction (Bragg's Law)

The wavelength of x-rays, \lambda, is roughly equal to the distance, d, between atom/ion layers. This allows x-rays to probe for d via Bragg's Equation:

Requirements for the x-rays:

• Monochromatic
• Coherent (phase difference of 2\pi n where n is any integer)
• Parallel with each other

The incoming x-rays 1 and 2 strike the rows of ions in the crystal and are diffracted, which can be considered reflection at the atomic level. The angle of incidence equals the angle of reflection.

The outgoing x-rays 1 and 2 are coherent only if the extra path travelled by ray 2, $2d\sin\theta$ is any multiple, n, of \lambda. Or:

n\lambda = 2d\sin\theta

This is Bragg's Law.

Metals

Defects on the Atomic Scale

Defects on the atomic scale have a significant effect on yield stress, ultimate tensile stress, and ultimate fracture stress.

The yield stress of a real metal(-alloy) is much lower than the theoretical yield stress for the perfect metal(-alloy) crystal. This difference is because of the defects in the metal, particularly dislocations, as the dislocations allow the ions to slide past each other at much lower yield stresses.

The 5 types of defects are:

• Grain boundaries
• Vacancies (missing ion)
• Dislocations (missing row of ions)
• Impurity ions
• Crystalline includison

Dislocation Movement vs. Simple Sliding

The layers of ions in a crystalline metal could simply over each other:

However, the stress required for simple sliding is much higher than the stress required to move a dislocation. This is because dislocation motion is successive sliding of the partial plane of ions under applied shear stress (black arrow). The vacancy in the slip plane (yellow arrow) moves in steps in sequence from left to right.

If there are no dislocations then plastic deformation is delayed to a higher applied stress, meaning the yield stress of the metal would be much higher.

Dislocations move more easily on specific planes and in specific directions called the slip planes and slip directions which make up what is known as the slip system.

There are a very large amount of dislocations in metals and alloys. Dislocation density is expressed as total length of dislocations per unit volume.

Single Crystal Metals

Normally when a molten metal is cooled to a solid, then lots of tiny crystals (grains) grow in different directions until they impinge. The grain boundaries are a source of mechanical weakness.

A single crystal metal is one for which the casting is cooled to form just one giant crystal:

1. The molten metal is cast into a mould
2. At the very base of the mould, the temperature is dropped and the alloy crystallises into many little crystals
3. The crystals grow upwars through the liquid and meet a spiral tube and are constricted
4. This tube only allows one crystal to grow through the spiral and then into the main mould

Polycrystalline Metals

Most normal metals you see everyday are polycrystalline.

Elastic and Plastic Strain in Metals

When you apply a tensile stress to a mteal, this will produce a shear stress in any part of the metallic lattice that is not parallel or perpendicular to the applied stress. Under the action of shear stress, the metallic lattice will tend to experience a combination of elastic strain and plastic strain:

Raising the Yield Stress of a Metal

There are 4 main ways to raise the yield stress of a metal:

• Make a solid-solution---by metal alloying or atomic addition
• Precipitate crystalline inclusions---by metal alloying or atomic additions and then heat treatment
• Work-harden --- by processing and/or cold-working
• Decrease the grain size --- by processing and/or heat-treatment

Make a Solid-Solution

Adding an alloying element, B, to the host, A, forms a solid-solution as the ions or atoms of B dissolve in A.

The impurity particles of B are a different size from the particles of A, distorting the metal lattice. The larger the difference in radii of the particles, the bigger the distortion.

The particles of B tend to diffuse to dislocations and immobilise them. This is why alloying increases the yield stress.

Impurity particles generate lattice strain in the structure too:

• Smaller particles introduce a compressive strain in the surrounding lattice
• Larger particles introduce a tensile strain in the surrounding lattice

Precipitating Crystalline Inclusions

When adding an element, B, to a host, A, exceeds the solubility, the result is the formation of a solid-solution with a fixed ratio of B to A, but also precipitated crystals of a different ratio of B to A.

Crystalline inclusions are really difficult to shear, especially if they are small, numerous, and have high Vickers' hardness. This slows down dislocation movement, increasing yield stress.

Work-Hardening and Cold Working

We can use room temperature deformation to increase the number of dislocations present in a metal. As the % cold-work (%CW) is increased, the number of dislocations present also increases:

\% CW = \frac{A_0 - A_d}{A_0} \times 100\%

where A_0 is the initial cross sectional area and A_d is the final cross sectional area.

A carefully prepared sample has a dislocation density, \rho_d of around 10^3 mm mm$3$, whereas for a heavily deformed sample it is around 10^{10}.

A high density of dislocations means they are more likely to get entangled with each other, making it harder for dislocations to move. Therefore as \rho_d increases, yield stress does too.

Decreasing the Grain Size

• Most metals are polycrystalline with many grains.
• Different grains will have a different crystal orientation.
• Grains impede dislocation motion

As you decrease grain size, you get more grain boundaries which basically creates more barriers to prevent slip.

This is because a dislocation would have to change orientation across a grain boundary and "ionic disorder in the grain boundary results in discontinuity of slip" (A.B Seddon, University of Nottingham 2020) (I think that's repeating it but it said it on the slideshow sooo...).

So for any given metal, the fine grained is harder and has greater yield stress than the coarse grained version of it.

Hall Petch Equation

\sigma_{yield} = \sigma_0 + k_yd^{-0.5}

where d is the grain size and \sigma_0 and k_y are material constants.

Therefore a plot of \sigma_{yield} against d^{-0.5} would results in a straight line.

Heat Treatment of Metals

These processes are to change a material's mechanical properties, not change its shape.

Phase Diagrams

Here is an example of a two component phase diagram with a familiar system:

The component in this case are sugar and water, but not syrup.

A phase is a chemically and physically distinct species as we can have a change in phase that goes from solid to solid.

The solubility limit is the maximum concentration for which only a solution occurs. In the case of this system, thee limit increases with temperature.

Here is a generic phase diagram for a generic A-B system:

• L - liquid
• \alpha --- a solid phase but still a solution. B can dissolve into A
• \beta --- a solid phase but still a solution. A can dissolve into B

Annealing

Annealing is a process by which a component is heated to remove the effects of cold work.

These are diffusional processes and only occur at high temperatures. The driver for diffusion is the removal of high energy defects from the system.

Diffusion

Diffusion is atomic or ionic movement down a concentration gradient.

Solid State Diffusion

Solid state diffusion is the stepwise migration (march) of atoms or ions through a lattice, from site to site.

In order for this to happen, there must an adjacent vacant site. The diffusion particle must also have sufficient thermal energy to 'jump' to the new site.

Vacancy Diffusion (Diffusion of Metal Ions)

Interstitial DIffusion (Diffusion of Small, Non-Metallic Particles)

The Math(s) of Diffusion

Diffusion is time dependent.

For steady state diffusion, Fick's 1st Law holds:

J = -D \frac{\mathrm{d}C}{\mathrm{d}x}

where J is the flux, \frac{\mathrm{d}C}{\mathrm dx} is the concentration gradient, and D is the constant of proportionality known as the diffusion coefficient.

D is constant for a particular metal at a particular temperature. The fluxis the number of atoms or ions moving per second through a cross sectional area.

Things that Affect the Speed of Diffusion

• size of the diffusion species --- smaller species results in faster diffusion

• temperature --- more thermal energy allows more particles to have enough energy to make the 'jump'

• host lattice

  • simple cubic --- 52% occupancy of ions
  • body centered cubic --- 68% occupancy of ions
  • face centered cubic --- 74% occupancy of ions

  Diffusion is faster in a BCC host than in an FCC host for iron ions in an iron host and also for carbon atoms diffusing into an iron host. However this is not always the case.

Influence of Temperature on Diffusion (Arrhenius Equation)

You can apply the Arrhenius equation for all thermally activated diffusion:

D = D_0 \exp{\left( - \frac{Q}{RT} \right)}

where D is the diffusion coefficient, D_0 is the frequency factor, Q is the activation energy, R is the ideal gas constant (8.31 J k$^{-1}$ mol$^{-1}$).

You can find the diffusion distance, x, with the following equation:

x ~ \sqrt{Dt}

Materials in Sustainable Transport

• Concerns over use of fossil fuels, climate change
• Const of energy
• Energy use in making and moving vehicles
• Rising energy prices mean cost of fuel is comparable to cost of car
• 1/4 of energy used in UK is to transport goods and people
• Legislation and voluntary targets set by EU to improve fuel efficiency
• In 2015 average CO2 emmisions as 130 g / km
• Engine powerhas gone up significantly from 2001 to 2018 (~30%) yet engine displracement has gone down ~10% and CO2 emissions down ~18% while weight has gone up ~10%

Is the car emissions reduction target significant?

Overall CO2 emissions in 2016 is 466 Megatonnes.

Does a reduction from 130 g / km to 95 g / km (a 35 g/km reduction) make a significant difference?

There are 33 million registered cars in the uk.

If they average around 8000 miles each (~13000 km) per year that's a ~15 Megatonne reduction, or about 3% of the annual C02 emmissions, a significant reduction.

Materials in Cars

• Most of the energy used by cars is during driving (71%)
• This means the mass of the vehicle has a great effect on its emmissions across a lifetime
• The body, suspension, drivetrain, and interior all contribute roughly a quarter to the mass of the car
• However, the mass of cars are increasing

Material Substitution

• The material will likely have performance requirements:

  • It may need to be a physical size
  • It may need to operate at certain temperatures
  • It may need to bear a certain load

• The component mustalso be designed for convenient manufacturing, assembly, servicing, disposal, remanufacturing and/or disassembly

Case Study --- 2012 Honda Accord

• Body --- opted to stay with steel --- aluminium intense and multi-material approaches were both rejected due to higher costs and limitations in manufacturing and assembly. Recyclability was also noted as an issue due to different grades of aluminium needing to be separated at end of life.
• Doors and bonnets --- move to aluminium from steel --- more costly but the mass savings made this option worth it
• Wiring --- aluminium to copper --- lower mass for same conductivity, copper is more expensive (I think)
• Seats --- steel to composites or magnesium structural components --- very high weight savings

Choosing a Material

Glossary

• liquidus - for a system of more than one component, the liquidus is the lowest temperature at which the whole system is all in the liquid state.
• solidus - for a system of more than one component, the solidus is the highest temperature at which the whole system is still in the solid state